UNIVERSIDAD NACIONAL DE SAN AGUSTN DE AREQUIPA
FACULTAD DE INGENIERA DE PROCESOS
ESCUELA PROFESIONAL DE INGENIERA METALRGICA
7/29/2019 2 Preparacin 2012
2/85
EPIMAT-UNSA
2
Cap. 2 Tcnicas de Preparacin de Muestras
Cap. 2 Tcnicas de Preparacin de Muestras2.1. Introduccin
2.2. Objetivos y Parmetros de Preparacin de Muestras
2.3. Extraccin de Muestras2.4. Seccionamiento de Muestras
2.5. Montaje de Muestras
2.6. Desbaste y Pulido Mecnico
2.7. Pulido Qumico y Electroltico2.8. Tcnicas de contraste y Ataque
7/29/2019 2 Preparacin 2012
3/85
Etapas de preparacin: muestreo,
seccionamiento, y
preparacin de la superficie
Criterios de preparacin de una muestra
Preparacin Sistemtica: reglas para muestras similares
Reproducibilidad del mtodo de preparacin y el control de
los parmetros (rpp, fuerza, aditivos, tiempo)
Estructura real: caractersticas de la superficie preparada
Resultados aceptables de la preparacin
EPIMAT-UNSA
3
Cap. 2 Tcnicas de Preparacin de Muestras
7/29/2019 2 Preparacin 2012
4/85
Remover la deformacin inducida por el seccionamiento,
desbaste y pulido.
Eliminar las rayas del desbaste inicial.
Evitar la formacin de huecos, erosin, agrietamiento de
partculas duras, manchas y otros defectos de preparacin.
Minimizar el relieve
La superficie debe ser plana, particularmente en los bordes.
Se deber mantener planas las superficies revestidas
EPIMAT-UNSA
4
Cap. 2 Tcnicas de Preparacin de Muestras
7/29/2019 2 Preparacin 2012
5/85
Para revelar la estructura real de la muestra se deber
Eliminar la deformacin inducida por corte, esmerilado y pulido o
debe ser poca profunda para que sea eliminada por el reactivo de
ataque (rayas, extracciones, picaduras, grietas, manchas, relieves, etc.)
limpiar las muestras entre las etapas de preparacin, despus de lapreparacin y despus del ataque.
El atacante seleccionado debe ser o general o selectivo en su accin
para producir fases o lmites de grano limpios, precisos y un contraste
alto.
EPIMAT-UNSA
5
Cap. 2 Tcnicas de Preparacin de Muestras
7/29/2019 2 Preparacin 2012
6/85
La preparacin de muestras materialogrficas requiere de
cinco operaciones:
corte,
montaje (opcional),
esmerilado,
pulido y
Ataque (opcional)
EPIMAT-UNSA
6
Cap. 2 Tcnicas de Preparacin de Muestras
7/29/2019 2 Preparacin 2012
7/85
EPIMAT-UNSA
7
Cap. 2 Tcnicas de Preparacin de Muestras
7/29/2019 2 Preparacin 2012
8/85
Superficie del disco o paos Usar el recomendado por el mtodo a aplicarse
Abrasivo debe tener una dureza de 2.5 a 3 veces la dureza del material a ser
preparado
Tamao de grano del abrasivo al inicio ms pequeo y entre etapas, el intervalo ms grande posible.
Lubricante
alta cantidad con poca cantidad de abrasivo para materiales blandos, menos cantidad con alto contenido de abrasivo para materiales duros,
el pao debe estar hmedo pero no mojado
EPIMAT-UNSA
8
Cap. 2 Tcnicas de Preparacin de Muestras
7/29/2019 2 Preparacin 2012
9/85
Velocidad rotacional usar la recomendada de acuerdo al material a prepararse
Fuerza
El rea de la muestra montada deber ser 50% del soporte
Tiempo Debe ser lo mas corto posible, examinar cada minuto
EPIMAT-UNSA
9
Cap. 2 Tcnicas de Preparacin de Muestras
7/29/2019 2 Preparacin 2012
10/85
EPIMAT-UNSA
10
Cap. 2 Tcnicas de Preparacin de Muestras
7/29/2019 2 Preparacin 2012
11/85
La muestra debe ser representativa del material a caracterizar Todos los procesos de seccionamiento producen dao;algunos mtodos (como el oxicorte o corte abrasivo seco)
producen cantidades extremas de daos.
Las normas ASTM E 45, E 1122 y 1245 E aconsejan que sebene tomar varias muestras para estudiar las inclusiones enaceros.
Para estudiar el tamao de grano, es comn usar una muestrade un lote.
Para estudiar el efecto de la deformacin en la forma delgrano de los metales forjados, se requiere tomar un mnimode dos secciones - una perpendicular a, y otro paralelo a, ladireccin de deformacin
EPIMAT-UNSA
11
Cap. 2 Tcnicas de Preparacin de Muestras
7/29/2019 2 Preparacin 2012
12/85
EPIMAT-UNSA
12
Cap. 2 Tcnicas de Preparacin de Muestras
Mtodos de seccionamiento muestras metalogrficas
7/29/2019 2 Preparacin 2012
13/85
EPIMAT-UNSA
13
Cap. 2 Tcnicas de Preparacin de Muestras
Mtodos dependiente de la profundidad deformacin de corte del metal
7/29/2019 2 Preparacin 2012
14/85
EPIMAT-UNSA
14
Cap. 2 Tcnicas de Preparacin de Muestras
7/29/2019 2 Preparacin 2012
15/85
7/29/2019 2 Preparacin 2012
16/85
EPIMAT-UNSA
16
Cap. 2 Tcnicas de Preparacin de Muestras
La seleccin del disco abrasivo es importante evitar la introduccinde niveles innecesarios de dao al cortar las muestras
7/29/2019 2 Preparacin 2012
17/85
EPIMAT-UNSA
17
Cap. 2 Tcnicas de Preparacin de Muestras
Materiales Disco de corte: abrasivo/ligante
Acero, materiales ferrosos, aceros
endurecidosAl2O3 (corundum)/bakelita
Aceros de alta aleacin Nitruro de boro cbico (CBN)/bakelitaMetales no ferrosos, metales duros Carburo de silicio (SiC)/bakelita
Materiales duros y tenaces, cermets,
cermicosDiamante/bakelita
Materiales duros y frgiles, ceramicos,
minerales
Diamante/metal
7/29/2019 2 Preparacin 2012
18/85
7/29/2019 2 Preparacin 2012
19/85
7/29/2019 2 Preparacin 2012
20/85
EPIMAT-UNSA
20
Cap. 2 Tcnicas de Preparacin de Muestras
Limitado a materiales o compuestos conductres que tienen una cantidad
menor de materiales no conductores.
Se utiliza para seccionar metales duros, metales con cristales simples y
para cortar tambin cermicos.
nodo
7/29/2019 2 Preparacin 2012
21/85
EPIMAT-UNSA
21
Cap. 2 Tcnicas de Preparacin de Muestras
En el caso de materiales con baja conductividad trmica y baja resistencia
a la fractura (por ejemplo, vidrios y cermicos) el proceso est
acompaado por un choque trmico considerable.
7/29/2019 2 Preparacin 2012
22/85
EPIMAT-UNSA
22
Cap. 2 Tcnicas de Preparacin de Muestras
metales duros, fundicin gris
o vidrios y cermicos
7/29/2019 2 Preparacin 2012
23/85
Probablemente, el mtodo ms cuidadoso para el corte demetales no metales con enlace inico con casi ningn dao enla superficie
El corte y fresado se realiza con hilos o cuerdas infiltrados concido o con chorros de cido de 150 m de ancho.
El procedimiento es asistido con electricidad con el uso de unhilo o boquilla como ctodo y la muestra como nodo.
Estos tratamientos toman bastante tiempo y as se limitan a loscristales individuales de corte o de secciones
Estos tratamientos toman bastante tiempo y por lo tanto estnlimitados al corte de monocristales o de secciones delgadas.
EPIMAT-UNSA
23
Cap. 2 Tcnicas de Preparacin de Muestras
7/29/2019 2 Preparacin 2012
24/85
EPIMAT-UNSA
24
Cap. 2 Tcnicas de Preparacin de Muestras
Materiales biolgicos, polmeros
7/29/2019 2 Preparacin 2012
25/85
EPIMAT-UNSA
25
Cap. 2 Tcnicas de Preparacin de Muestras
Montaje de muestras en un dispositivo de sujecin es necesario cuando se
preparan muestras irregulares, pequeas, muy blandas, frgiles, y en los
casos en que se requiere una retencin de borde.
7/29/2019 2 Preparacin 2012
26/85
7/29/2019 2 Preparacin 2012
27/85
EPIMAT-UNSA
27
Cap. 2 Tcnicas de Preparacin de Muestras
7/29/2019 2 Preparacin 2012
28/85
7/29/2019 2 Preparacin 2012
29/85
EPIMAT-UNSA
29
Cap. 2 Tcnicas de Preparacin de Muestras
(a) molde flexible. (b) molde de plstico
7/29/2019 2 Preparacin 2012
30/85
7/29/2019 2 Preparacin 2012
31/85
EPIMAT-UNSA
31
Cap. 2 Tcnicas de Preparacin de Muestras
Easy-to-use resins with short curing times
Negligible shrinkage
7/29/2019 2 Preparacin 2012
32/85
EPIMAT-UNSA
32
Cap. 2 Tcnicas de Preparacin de Muestras
Curing times are relatively short and the hardened sample is duroplastic
7/29/2019 2 Preparacin 2012
33/85
7/29/2019 2 Preparacin 2012
34/85
EPIMAT-UNSA
34
Cap. 2 Tcnicas de Preparacin de Muestras
Two mounts can be produced at one time using the duplexing spacer.
Cycle times range from 8-12 minutes.
7/29/2019 2 Preparacin 2012
35/85
EPIMAT-UNSA
35
Cap. 2 Tcnicas de Preparacin de Muestras
7/29/2019 2 Preparacin 2012
36/85
Requirements of hot and cold mounting materials Specimens thoroughly cleaned either with an ultrasonic cleaner orlightly brushed with water containing a detergent
Inert to the specimen, mold, and etchant
Moderate viscosity during the actual embedding process; nogeneration of air
bubbles after solidification Low linear shrinkage and good adhesion to the specimen
Grinding and polishing behavior similar to those of the specimen, aswell as
similar chemical resistance to all reagents used during the specimen
preparation
EPIMAT-UNSA
36
Cap. 2 Tcnicas de Preparacin de Muestras
7/29/2019 2 Preparacin 2012
37/85
7/29/2019 2 Preparacin 2012
38/85
EPIMAT-UNSA
38
Cap. 2 Tcnicas de Preparacin de Muestras
Hot compression mountingmaterials
Cold/room-temperature-curing
Thermosetting plasticsPhenol resins (Bakelite)
Epoxy resinsDiallyl phthalate
Epoxy resins
Polyester resins
Polymerization is irreversible;
material cannot resoften. Heat to
~150 C under pressure. Samples
can be removed hot from themounting press, but cooling under
pressure is recommended.
Polymerization is irreversible; material
will not resoften. Hardening reaction may
increase the temperatures! This is directly
related to the mixing ratio, the ambienttemperatures, the volume of the mixed
components, and the heat transfer by the
molds.
Comparison of hot and cold mounting materials
7/29/2019 2 Preparacin 2012
39/85
7/29/2019 2 Preparacin 2012
40/85
7/29/2019 2 Preparacin 2012
41/85
EPIMAT-UNSA
41
Cap. 2 Tcnicas de Preparacin de Muestras
Properties of some important mounting materials
Material PropertyCold mounting materialsEpoxy
resins
Good adhesion. High viscosity, fills cracks, gaps, and pores easily
and is therefore well suited for infiltration. Resistant to etchants
and solvents. Nearly transparent. Mold material should be madeof silicon rubber, polyethylene, or Bakelite. Curing time at least 8
h. Work under a fumehood because poisonous fumes are being
generated. Skin irritant
Polyester
resins
Good abrasion resistance, therefore well suited for hard materials.
Shrinkage. Chemical resistance varies with the product.
Acrylics Shrinkage. Short curing times. Poor resistance to alcohol and
chlorohydrocarbon
7/29/2019 2 Preparacin 2012
42/85
EPIMAT-UNSA
42
Cap. 2 Tcnicas de Preparacin de Muestras
When the thickness of the coated sample is known (Fig. 3.19a), thenthe following equation applies: L = S L/S, or
if the angle (Fig. 3.19b) ofthe supporting wedge is known, then L =L sin
7/29/2019 2 Preparacin 2012
43/85
When analyzing thin layers and surface defects, it is importantto have a sample with good edge retention
Rinsing the sample with a wetting agent and using a material
generating low shrinkage during the curing cycle is beneficial
the sample surface is reinforced with an additional layer.
By addition of ceramic particles, such as alumina powder, thehardness of the mounting material can be increased and
adjusted to the hardness of the sample
EPIMAT-UNSA
43
Cap. 2 Tcnicas de Preparacin de Muestras
7/29/2019 2 Preparacin 2012
44/85
the sample must have an electric contact.
This can either be a hole drilled through the mounting materialor a wire attached to the sample before mounting
They are plastic materials, to which metal powders such asiron, silver, copper, or graphite have been added.
Another excellent technique is to embed the sample in low-melting bismuth alloys
EPIMAT-UNSA
44
Cap. 2 Tcnicas de Preparacin de Muestras
7/29/2019 2 Preparacin 2012
45/85
EPIMAT-UNSA
45
Cap. 2 Tcnicas de Preparacin de Muestras
7/29/2019 2 Preparacin 2012
46/85
EPIMAT-UNSA
46
Cap. 2 Tcnicas de Preparacin de Muestras
Specimens with voids, pores, and small cracks, and sample material that
are fragile or brittle are prone to breakouts
Only Epoxy resins can be used for vacuum impregnation due to their low
viscosity and their low vapour pressure
7/29/2019 2 Preparacin 2012
47/85
Metal powders with a particle size above 2 m should be coldmounted in epoxy resin with pressurizing equipment.
Powders that tend to agglomerate with a particle size less than2 m (e.g., ceramic powders) can be embedded as follows:
the powder is placed in a test tube and put under vacuum with a three-
way tap using running water;
it is then infiltrated with a mixture of methacrylic acid methyl ester and
1% (wt%) of benzole peroxide.
This mixture cures in 12 h at 50C, with the test tube kept closed. The test tube is then broken and the powder sample is processed as
usual.
EPIMAT-UNSA
47
Cap. 2 Tcnicas de Preparacin de Muestras
7/29/2019 2 Preparacin 2012
48/85
EPIMAT-UNSA
48
Cap. 2 Tcnicas de Preparacin de Muestras
Mechanisms of material removal
7/29/2019 2 Preparacin 2012
49/85
7/29/2019 2 Preparacin 2012
50/85
Proper grinding removes damaged or deformed surfacematerial, while introducing only limited amounts of new
deformation..
The lapping process is an alternative to grinding, in which theabrasive particles are not firmly fixed to paper. Instead a pasteand lubricant is applied to the surface of a disc..
Grinding can be divided into two individual processes:
plane grinding and fine Grinding
EPIMAT-UNSA
50
Cap. 2 Tcnicas de Preparacin de Muestras
7/29/2019 2 Preparacin 2012
51/85
7/29/2019 2 Preparacin 2012
52/85
EPIMAT-UNSA
52
Cap. 2 Tcnicas de Preparacin de Muestras
Copper specimen ground with 180 grit paper
7/29/2019 2 Preparacin 2012
53/85
7/29/2019 2 Preparacin 2012
54/85
EPIMAT-UNSA
54
Cap. 2 Tcnicas de Preparacin de Muestras
Copper specimen ground with 800 grit paper
7/29/2019 2 Preparacin 2012
55/85
EPIMAT-UNSA
55
Cap. 2 Tcnicas de Preparacin de Muestras
Copper specimen ground with 1200 grit paper
7/29/2019 2 Preparacin 2012
56/85
EPIMAT-UNSA
56
Cap. 2 Tcnicas de Preparacin de Muestras
7/29/2019 2 Preparacin 2012
57/85
EPIMAT-UNSA
57
Cap. 2 Tcnicas de Preparacin de Muestras
7/29/2019 2 Preparacin 2012
58/85
EPIMAT-UNSA
58
Cap. 2 Tcnicas de Preparacin de Muestras
Manual grinder/polisher
machine
7/29/2019 2 Preparacin 2012
59/85
EPIMAT-UNSA
59
Cap. 2 Tcnicas de Preparacin de Muestras
conducted with particles of6- or 3-m
7/29/2019 2 Preparacin 2012
60/85
EPIMAT-UNSA
60
Cap. 2 Tcnicas de Preparacin de Muestras
With particles of 1-m
7/29/2019 2 Preparacin 2012
61/85
EPIMAT-UNSA
61
Cap. 2 Tcnicas de Preparacin de Muestras
Copper specimen polished to 6 micron level
7/29/2019 2 Preparacin 2012
62/85
EPIMAT-UNSA
62
Cap. 2 Tcnicas de Preparacin de Muestras
Copper specimen polished to 1 micron level
7/29/2019 2 Preparacin 2012
63/85
Specimen Movement: rotate in a direction counter to the rotation of the polishing wheel.
the specimen is continually moved back and forth between the centerand the edge of the wheel,
After each step, the specimen is rotated 45 to 90 so that the abrasion is
not unidirectional Polishing Pressure The correct amount of applied pressure must be determined by
experience
EPIMAT-UNSA
63
Cap. 2 Tcnicas de Preparacin de Muestras
7/29/2019 2 Preparacin 2012
64/85
7/29/2019 2 Preparacin 2012
65/85
7/29/2019 2 Preparacin 2012
66/85
7/29/2019 2 Preparacin 2012
67/85
EPIMAT-UNSA
67
Cap. 2 Tcnicas de Preparacin de Muestras
Vibratory polisher
7/29/2019 2 Preparacin 2012
68/85
Electrolytic polishing to grind the surface to a 600-grit finish and then electropolish for about
1- o 2-minutes
soft single-phase metals and alloys
Suitable electrolytes: diluted phosphoric, sulfuric or perchloric acid,acetic acid or alcohol
Chemical polishing The agents are usually strongly oxidizing
EPIMAT-UNSA
68
Cap. 2 Tcnicas de Preparacin de Muestras
7/29/2019 2 Preparacin 2012
69/85
EPIMAT-UNSA
69
Cap. 2 Tcnicas de Preparacin de Muestras
Circuitos elctricos y arreglos de los equipos usados para el pulido
electroltico
7/29/2019 2 Preparacin 2012
70/85
7/29/2019 2 Preparacin 2012
71/85
Combined techniques, such as alternating mechanical andelectrolytic polishing or etch-polishing, give improved results
in the case of soft or tough metals since deformation and
reaction layers at the surface of the sample are easily removed.
Moreover, refractory metals, multiphase alloys and coatedmaterials can be satisfactorily treated.
Etch-polishing is also applicable to some ceramics, e.g. grainboundary phases in AlN or Al2O3 become visible if NaOH is
added to the abrasive suspension
EPIMAT-UNSA
71
Cap. 2 Tcnicas de Preparacin de Muestras
7/29/2019 2 Preparacin 2012
72/85
7/29/2019 2 Preparacin 2012
73/85
7/29/2019 2 Preparacin 2012
74/85
EPIMAT-UNSA
74
Cap. 2 Tcnicas de Preparacin de Muestras
Etched copper specimen
7/29/2019 2 Preparacin 2012
75/85
7/29/2019 2 Preparacin 2012
76/85
EPIMAT-UNSA
76
Cap. 2 Tcnicas de Preparacin de Muestras
Specimen levelling press
7/29/2019 2 Preparacin 2012
77/85
EPIMAT-UNSA
77
Cap. 2 Tcnicas de Preparacin de Muestras
Heat Tinting: Grain structure of annealed CP titanium revealed by heat tinting on a hot
plate
7/29/2019 2 Preparacin 2012
78/85
EPIMAT-UNSA
78
Cap. 2 Tcnicas de Preparacin de Muestras
7/29/2019 2 Preparacin 2012
79/85
EPIMAT-UNSA
79
Cap. 2 Tcnicas de Preparacin de Muestras
Characteristic curve for an electrolytic cell
7/29/2019 2 Preparacin 2012
80/85
7/29/2019 2 Preparacin 2012
81/85
7/29/2019 2 Preparacin 2012
82/85
EPIMAT-UNSA
82
Cap. 2 Tcnicas de Preparacin de Muestras
Microstructure of thermally etched Al2O3-15 vol.% ZrO2 ceramic. The
white particles are zirconia
7/29/2019 2 Preparacin 2012
83/85
EPIMAT-UNSA
83
Cap. 2 Tcnicas de Preparacin de Muestras
Effect of ion milling on titanium. Mechanically prepared surface on left and
ion milled surface on right
7/29/2019 2 Preparacin 2012
84/85
EPIMAT-UNSA
84
Cap. 2 Tcnicas de Preparacin de Muestras
Instead of an epoxy resin,
Canadian Balsam is often
used, especially if the index of
refraction of the resin has to be
known
In geosciences, the thicknessof the thin section is
normalized to 20-30 m
according to the interference
colors of quartz.
For the characterization ofceramics the thickness may be
chosen according to the
particle size
7/29/2019 2 Preparacin 2012
85/85
EPIMAT-UNSA
85
Preparation of thin sections